What is Round Bar?

Round bars are thick, pre-finished metal products that come with a circular base. Also referred to as bar stocks, round bars are primarily used in applications that require shafts or rods. They may be manufactured in different diameters — from ¼-inch to large, 24-inch thick stocks for heavier-duty use to Round Bar Manufacturers.

For this reason, round bars have to be made out of durable raw metal or alloy, such as steel, aluminum, iron, or titanium. Industries may depend on either one or two of these metals, nevertheless, the advantages of round bars continue to make them one of the most formidable materials to achieve excellent load-bearing capacities and aesthetic finish by Round Bar Manufacturers.

Materials for Round Bar

Specifications of Round Bars

Range	3.17 MM TO 350 MM DIA
Diameter	25MM TO 152 MM
Condition	Cold Drawn & Polished Cold Drawn, Centreless Ground & Polished
Form	Round, Square, Hex (A/F), Rectangle, Wire (Coil Form), Wire-Mesh, Billet, Ingot, Forging Etc.

Round Bar Chemical Composition

Grade	Carbon	Manganese	Silicon	Phospherous	Sulfur	Chromium	Molybdenum	Nickel	Nitrogen
SS 304	0.08 max	2 max	0.75 max	0.040 max	0.030 max	18 – 20	-	8 – 11	-
SS 304L	0.03 max	2 max	0.75 max	0.045 max	0.030 max	18 – 20	-	8 – 12	0.10 max

Round Bar Mechanical Properties

Density	Melting Point	Yield Strength (0.2%Offset)	Tensile Strength	Elongation
8.0 g/cm3	1400 °C or (2550 °F)	Psi – 30000 , MPa – 205	MPa – 515, Psi – 75000	35%
8.0 g/cm3	Psi – 30000 , MPa – 205	1400 °C (2550 °F)	Psi – 75000 , MPa – 515	40%